ANTI F 750ml Ceramic Clay Self-cleaning & antifouling

High antifouling technology self-cleaning Surface paint, 1-component, for all types of boats (Wooden, Polyester, Metal) with a maximum speed of up to 25 nautical miles.

• It is applied to the hull, below the waterline, and due to its high content of copper oxides it prevents the growth of marine organisms such as oysters and algae which, together with ANTI F, detach from the boat as it travels (self-cleaning).
• In this way the hull is not only kept clean but also smooth so as not to add friction to the boat ensuring high sailing speeds and engine efficiency reducing fuel costs.

• Appearance: Matt, Gloss 0-10% - Lange Gloss (at 600 angle) according to ISO 2813
• Metal Surface Temperature Resistance: 50 °C
• Recommended Dry Film Thickness: 75-100 µm, per layer. It is recommended that the total dry top coat thickness is 125 µm or 150 µm, for durability of 24 or 36 months respectively
• Theoretical Coverage: 9.5 m2/liter = 50 μm4.75 m2/liter = 100 μm
• Full Polymerization: 24 hours
• Minimum Repainting Time (at 25°C and 65 %RH): 5 hours for 50 µm. At larger paint thicknesses, the repainting time is considerably longer
• Maximum Repainting Time: 30 hours at 25°C but depends on ambient temperature

• For all sizes of boats from small boats to yachts, passenger boats, tugboats etc.
• For all surfaces – Wood, Polyester, Metal
• Excellent resistance to permanent immersion in the sea
• Protection from marine microorganisms on the reefs of boats with a minimum sailing speed of 2 n.m. up to 25 n.m. maximum
• Self-cleaning
• Provides protection from 1 to 3 years depending on paint thickness and local factors such as water temperature and salt content
• Environmentally friendly as it is manufactured without the banned biocide TBT and in accordance with the laws of IMO  for the ground colors