ANTI F 1L. Self-cleaning reef tile

High anti-pollution technology self-cleaning reef paint, 1-component, for all types of boats (Wooden, Polyester, Metal) with a maximum speed of up to 25 nautical miles. It is applied to the hull, below the waterline, and due to its high content of copper oxides prevents the growth of marine organisms such as oysters and algae that together with ANTI F detach from the boat as it travels (self-cleaning). In this way, the hull is not only kept clean but also smooth so that no friction is added to the boat ensuring high cruising speeds and engine efficiency while reducing fuel costs.

Appearance: Matte, Gloss 0-10% - Lange Gloss (at an angle of 600) according to ISO 2813
Metal Surface Temperature Resistance: 50 ° C
Recommended Dry Film Thickness: 75-100 μm, per layer. It is recommended that the total dry shelf thickness be 125 μm or 150 μm, for durability for 24 or 36 months respectively
Theoretical Coverage: 9.5 m2 / liter = 50 μm 4.75 m2 / liter = 100 μm
Full Polymerization: 24 hours
Minimum Repaint Time (at 25 ° C and 65% RH): 5 hours for 50 μm. At higher paint thicknesses, the repainting time is significantly longer
Maximum Repaint Time: 30 hours at 25 ° C but depends on ambient temperature.

• For all boat sizes from small boats to yachts, passenger boats, tugs etc.
• For all surfaces - Wood, Polyester, Metal
• Excellent resistance to permanent immersion in the sea
• Protection from marine microorganisms on the reefs of boats with a minimum cruising speed of 2 n.m. up to 25 n.m. maximum
• Self-cleaning
• Provides protection from 1 to 3 years depending on the paint thickness and local factors such as water temperature and salt content.
• Environmentally friendly as it is manufactured without the banned biocidal product TBT and in accordance with IMO legislation on reef paint